Tableted Products
Aluminium Degassing Tablets
|
TYPES OF DGASSER
|
FUNCTION
|
ALLOY TYPE
|
APPLICATION
|
APPLICATION
RATE
|
COLOUR
|
|
DGASSER-19
|
Degassing cum grain refining
|
All
|
Foundry / diecasting units
|
0.1 to 0.2% by weight of molten metal
|
Blue
|
|
DGASSER-20
|
Degassing
|
All
|
Extrusion/Properzy/Foundry
|
0.1 to 0.2% by weight of molten metal
|
Violet
|
|
DGASSER-20A
|
Strong Degassing
|
All
|
Alloy mfg/Extrusion
Foundry
|
0.1 to 0.2% by weight of molten metal
|
White
|
STANDARD PACKING: 20 Kg C.Box (Tablet
sizes 50 / 100 / 250 / 500 gms)
RANGE OF GRAIN REFINING
TABLETS FOR ALUMINIUM & MAGNESIUM ALLOYS
|
TYPES
|
FUNCTION
|
ALLOY TYPE
|
APPLICATION
|
APPLICATION
RATE
|
COLOUR
|
|
TIBON-5
|
Strong grainrefinement by Titanium/Boron
nucleation 5:1 ratio.
|
All Aluminium Alloys,
Low silicon Alloys.
|
|
0.1 to 0.2% by weight of molten metal
|
White
|
|
TIBON-5E
|
Grainrefinement by Titanium/Boron nucleation 5:1
ratio. Specially developed for Extrusion Plants.
|
All Aluminium Alloys,
Low silicon Alloys.
|
|
0.1 to 0.2% by weight of molten metal
|
White
|
|
TIBON-100
|
Nucleation by Boron only to give maximum
conductivity.
|
High conductivity Aluminium & casting alloys
containing Ti>0.15%
|
|
0.1 to 0.2% by weight of molten metal
|
White
|
|
TIBON-200
|
Nucleation by Titanium only
|
All Aluminium alloys where Ti is required in
compostition
|
|
0.1 to 0.2% by weight of molten metal
|
White
|
|
TIBON-P
(Powder Form)
|
Nucleation by Phosphorus. More effective &
safe than Red Phosphorous based grainrefiner.
|
Hyper Euctectic Al-Si Alloys recommended for All
Piston Alloys.
|
|
0.3 to 0.5% by weight of molten metal
|
White
|
STANDARD PACKING: 20 Kg C.Box ( Tablet
sizes 50 / 100 / 250 / 500 gms)
For Tibon-P packing is 5 KG P.Jar.
|